A large-grain-size thick-film polycrystalline diamond detector for x-ray detection

A diamond film with a size of 6 × 6 × 0.5 mm³ is fabricated by electron-assisted chemical vapor deposition. Raman spectrum analysis, x-ray diffraction and scanning electron microscope images confirm the high purity and large grain size, which is larger than 300 μm. Its resistivity is higher than ${10}^{12}\,{\rm{\Omega }}\cdot {\rm{cm}}.$ Interlaced-finger electrodes are imprinted onto the diamond film to develop an x-ray detector. Ohmic contact is confirmed by checking the linearity of its current–voltage curve. The dark current is lower than 0.1 nA under an electric field of 30 kV cm⁻¹. The time response is 220 ps. The sensitivity is about 125 mA W⁻¹ under a biasing voltage of 100 V. A good linear radiation dose rate is also confirmed. This diamond detector is used to measure x-ray on a Z-pinch, which has a double-layer 'nested tungsten wire array'. The pronounced peaks in the measured waveform clearly characterize the x-ray bursts, which proves the performance of this diamond detector.     

Making Large‐Area Titanium Disulfide Films at Reduced Temperature by Balancing the Kinetics of Sulfurization and Roughening

The synthesis of large‐area TiS₂ thin films is reported at temperatures as low as 500 °C using a scalable two‐step method of metal film deposition followed by sulfurization in an H₂S gas furnace. It is demonstrated that the lowest‐achievable sulfurization temperature depends strongly on the oxygen background during sulfurization. This dependence arises because Ti? O bonds present a substantial kinetic and thermodynamic barrier to TiS₂ formation. Lowering the sulfurization temperature is important to make smooth films, and to enable integration of TiS₂ and related transition metal dichalcogenides—including metastable phases and alloys—into device technology.     

Corrosion behaviour of Mg-Gd-Y-Zn-Ag alloy components with different sizes after cooling

The corrosion behaviour of Mg-6Gd-3Y-1Zn-0.3Ag (wt.%) alloy components with different sizes after cooling was investigated. The alloys in the small components (SC) cooled fast, which were composed of α-Mg matrix and coarse long-period stacking ordered (LPSO) phases. The alloys in the large components (LC) cooled slowly, and there were thin lamellar LPSO phases precipitating inside the grains, except for α-Mg matrix and coarse LPSO phases. The hydrogen evolution test revealed that the corrosion rate of LC sample was higher than that of SC sample. Electrochemical impedance spectroscopy (EIS) test showed that the surface film on LC alloys provided worse protection. The corrosion morphologies indicated that the precipitation of the thin lamellar LPSO phases in LC sample caused severe micro-galvanic corrosion, which accelerated the rupture of the surface film.     

Warpage control method during surface forming process of plastic film-reinforced flexible decorative veneer

The plastic film of the new plastic film reinforced pliable decorative veneer (PRPDSV) is used as a flexible reinforcement material and an adhesive material. It has good water resistance, impermeability, simple preparation and finishing processes, and no formaldehyde release. However, warpage phenomenon during hot pressing has been a bottleneck problem restricting its industrial development. In order to solve this problem solve, the study proposed a concave, and convex molds method, established an elastic–plastic FEA model of hot pressing processes of the PRPDSV using concave and convex molds with static/general static solution module in the nonlinear ABAQUS, and researched the effect on the performances of the PRPDSV from the parameters of temperature, pressure, and mold curvature radius theoretically and verified experimentally. Analysis results showed that the surface forming temperature had a great effect on warpage control for PRPDSV. The higher the temperature is, the smaller the curvature radius of the corresponding mold will be and the better the warpage will be. The curvature radius of the molds had a significant effect on the warpage control. Under the conditions with the same hot pressing parameters, the smaller the curvature radius is, and the better control on the warpage for the PRPDSV will be.     

Preparation and Characterization of Hydrophobic Bagasse Hemicellulose-based Films

To improve the hydrophobicity of bagasse hemicellulose-based films, glutaraldehyde was applied when preparing films of original and cationic bagasse hemicellulose with the addition of polyvinyl alcohol and sorbitol. The results showed that the cationic modification could increase the hydrophobicity of the hemicellulose-based film, and the hydrophobicity of hemicellulose-based films crosslinked with glutaraldehyde also increased. However, cationic modification of hemicellulose decreased the stress of the hemicellulose-based film. While crosslinking with glutaraldehyde increased the stress of both the original and cationic hemicellulose-based films. Macrophotography indicated that the film formability of the original hemicellulose was better than that of cationic hemicellulose. Through SEM observation, the degree of bonding of different components of the films was found to be increased due to crosslinking with glutaraldehyde. The crosslinking reaction between glutaraldehyde and hemicellulose was further confirmed by FT-IR spectroscopy.     

Investigations on hydrogen storage performances and mechanisms of as-cast TiFe0.8-mNi0.2Com (m=0, 0.03, 0.05 and 0.1) alloys

In order to improve the hydrogen storage performances of TiFe-based alloys, a new type of TiFe_0.8-mNi_0.2Co_m (m = 0, 0.03, 0.05 and 0.1) alloys were prepared through vacuum medium-frequency induction melting. XPS results showed that the composition of surface oxide film contains TiO₂, FeO and NiO for the cobalt-free alloy, and it also includes CoO and Co₃O₄ besides the above oxides for the cobalt-containing alloys. The activation temperature is 523, 403, 383 and 373 K for the TiFe_0.8-mNi_0.2Co_m (m = 0, 0.03, 0.05 and 0.1) alloys, respectively. The changes of the composition and microstructure of the surface oxide film are the root causes of the reduction of the activation temperature. XRD and SEM analyses showed that all the alloys are composed of the majority phase of TiFe phase and non-hydrogenated phase of Ti₂Fe phase. Adding appropriate amount of cobalt is beneficial to inhibiting the generation of Ti₂Fe phase and increasing the cell volume of TiFe phase. The hydrogenation capacity is proportional to the content of TiFe phase, which is 1.11, 1.48, 1.54 and 1.29 wt% for the TiFe_0.8-mNi_0.2Co_m (m = 0, 0.03, 0.05 and 0.1) alloys at 313 K, respectively. The hydrogenation plateau performance also is improved correspondingly.     

Inkjet-printed Ag@SDC core-shell nanoparticles as a high-performance cathode for low-temperature solid oxide fuel cells

This work demonstrates the superior thermostability of silver-based nanoparticle cathodes under continuous solid oxide fuel cell operation by coating the samarium-doped ceria (SDC) thin shell over silver nanoparticles. The Ag-core/SDC-shell (Ag@SDC) nanoparticles prepared by solvothermal synthesis (Ag core diameter = 48 nm; average SDC shell thickness = 2–5 nm) is inkjet-printed on electrolyte substrates as a thin film cathode. The Ag@SDC film survives the 48-h thermal annealing and its most porosities remain visibly un-agglomerated. The results of fuel cell current stability test show that the cell using the Ag@SDC nanoparticle cathode have only 3% of current degradation after 25 h, which is remarkably lower than that of the cell using the bare Ag nanoparticle cathode (96.1%). In addition, the electrochemical performance of the bare silver cathode in oxygen reduction reaction has significantly improved because of the enhanced surface oxygen adsorption/dissociation process provided by the SDC thin shell.     

透明红外硫系薄膜非均匀性检测及影响因素

薄膜非均匀性的无损检测对于制备大面积高质量的红外透明薄膜尤为重要。针对红外薄膜光学均匀性难以获取的困难,提出了一种同时获得单层透明红外薄膜厚度和折射率均匀性的无损检测方法。实验上,通过磁控溅射法在二氧化硅衬底上制备了厚度约1.4μm红外透明Ge-Sb-Se硫系薄膜,然后在该薄膜上标定出36个80μm×80μm区域,利用显微傅里叶红外光谱仪测得该36个区域的透射谱,通过分段滤波的方法滤除背景噪声,运用改进的Swanepoel方法计算得到了薄膜每一个区域的厚度和折射率,进而精确获得该薄膜的厚度和折射率均匀性,结果表明精度优于0.5%。